SEALUTION™ 210 Peel Polymer
| Category: | POP , Peel Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | SEALUTION™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7hf5Yh_SEALUTION-210-Peel-Polymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SEALUTION™ 210 Peel Polymer is a peelable sealant that gives a peelable seal to itself, polypropylene, and polyethylene. It is formulated for high clarity & low haze, which gives improved shelf appeal of finished films. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 1.5 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Seal Initiation Temperature 1(51 µm, Blown Film) | 105 | °C | Internal method |
| Peelable range 2 | 105 - 210 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.8 µm) | < 10 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Film thickness: 50 microns (2 mil) Coextruded blown film: A / B Coex, 80% / 20% layer ratio A = LLDPE/LDPE blend (40 µm / 1.6 mil) B = SEALUTION™ 210 (10 µm / 0.4 mil) Fabrication Conditions: Die Gap: 1.2 mm Melt Temperature: 180 to 230°C Blow-up ratio: 2.5 |
| Note Message | |
|---|---|
| 1 . | Temperatures at which 0.8 lb/in (2 N/15 mm) heat seal strength is achieved.Heat Seal Strengths, Topwave HT Tester 0.5 s dwell, 72.5 psi (5 bar) pressure, pull speed 3.9 in/sec (100 mm/sec). |
| 2 . | Peelable range of 2.3-3.4 lb/in (6-9 N/15 mm) for this particular structure, seal to itself. Peelable range of 1.9-2.7 lb/in (5-7 N/15 mm) for this particular structure, seal to PP sheet. Heat Seal Strengths, Topwave HT Tester 0.5 s dwell time, 72.5 psi (5 bar) pressure, pull speed 3.9 in/sec (100 mm/sec). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoPet 3510 | TechnoCompound GmbH | PET | TechnoPet |
| BITONER® C9 BP-100 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Sylvin 8494-87 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EPAMOULD EP90 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| Jieda PA610 Resin | Cixi Jieda Nanometer Compound Materials Co., LTD. | Nylon 610 | Jieda |