HANWHA LLDPE HS1600
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7hUMGn_HANWHA-LLDPE-HS1600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE HS1600 is high strength LLDPE manufactured by Unipol process and designed for stretch wrap. LLDPE HS1600 has excellent mechanical property, stretchability, optical properties and unwinding properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 44.1 | MPa | ASTM D882 |
| TD : Break, 20 µm | 39.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 750 | % | ASTM D882 |
| TD : Break, 20 µm | 850 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 200 | g | ASTM D1709B |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 20.0 µm | 117.7 | kN/m | ASTM D1004 |
| TD : 20.0 µm | 127.5 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Peak Melting Temperature | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 270 | °C |
| Extrusion instructions |
|---|
| Optimum Gage Range: 0.015 to 0.05 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2865 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 1400 GB 20 | RTP Company | PESU | RTP |
| TEKNIFLEX® Pouch PE2718 | Tekni-Films, a div of Tekni-Plex | Film, Polyester/PE/Al Foil/LLDPE | TEKNIFLEX® Pouch |
| INNOPOL® PP CS 2-3522 TO BU | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| LNP™ LUBRICOMP™ RP004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |