TAROLON 2500 W G6 X0
| Category: | PC , Polycarbonate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7hOf3O_TAROLON-2500-W-G6-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate medium viscosity, glass fiber reinforced 30%, self extinguishing UL94 V0, high stiffness, good mechanical properties also at high temperature, very good dimensional stability. UL 94 V0 approved all colors at 0,97 mm. UL746B approved. Available: all colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 to 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.15 to 0.20 | % | |
| Across Flow | 0.30 to 0.40 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 | % | ASTM D570, ISO 62 |
| Saturation | 0.20 | % | ASTM D570 |
| Saturation, 23°C | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7800 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 145 | MPa | ISO 178 |
| Break | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 9.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 3(23°C) | 40 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 148 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 75.0 | °C | UL 746B |
| -- 4 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | 158 | °C | ISO 306/A50, ASTM D1525 5 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 36 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 6x4x50 mm |
| 3 . | 6x4x50 mm |
| 4 . | 20000 hrs |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP520-4503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Dynacom CT-120 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| K PP 9073 AP | Technovinyl Polymers India Ltd. | PP, Unspecified | K PP |
| LNP™ STAT-KON™ JE006E compound | SABIC Innovative Plastics | PESU | LNP™ STAT-KON™ |
| SABIC® LDPE PCG02 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |