Generic MABS
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7hME1E_Generic-MABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic MABS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.16 | g/cm³ | ASTM D792 |
| 23°C | 1.08 - 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 2.0 - 19 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 13 - 23 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 2.00 - 8.05 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.40 - 0.55 | % | ASTM D955 |
| 23°C | 0.40 - 0.55 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 108 - 115 | ASTM D785 | |
| 23°C | 113 - 116 | ISO 2039-2 | |
| Ball Indentation Hardness | 70.0 - 76.3 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1950 - 2600 | MPa | ASTM D638 |
| 23°C | 1880 - 2720 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 42.9 - 51.4 | MPa | ASTM D638 |
| Yield, 23°C | 40.8 - 57.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 29.0 - 53.9 | MPa | ASTM D638 |
| Fracture, 23°C | 35.0 - 72.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 3.5 - 4.0 | % | ISO 527-2 |
| Fracture, 23°C | 10 - 40 | % | ASTM D638 |
| Fracture, 23°C | 9.7 - 20 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1800 - 2610 | MPa | ASTM D790 |
| 23°C | 1490 - 3000 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 55.0 - 85.4 | MPa | ISO 178 |
| Fracture, 23°C | 64.0 - 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.7 - 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 6.0 - 120 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 20 - 140 | J/m | ASTM D256 |
| 23°C | 2.0 - 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 83.8 - 92.2 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 77.0 - 92.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 72.4 - 78.4 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 - 105 | °C | ISO 306 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dissipation Factor (23°C) | 0.013 - 0.016 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.048 - 0.051 | % | |
| Rear Temperature | 205 | °C | |
| Middle Temperature | 215 | °C | |
| Front Temperature | 230 | °C | |
| Nozzle Temperature | 240 | °C | |
| Processing (Melt) Temp | 230 - 246 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Pressure | 126 - 156 | MPa | |
| Back Pressure | 1.23 - 1.26 | MPa | |
| Screw Speed | 49 - 50 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic MABSThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8240-98FU White 1513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Abstron IMC45 | Bhansali Engineering Polymers Limited | PC+ABS | Abstron |
| Chemraz 550 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Exceed™ 2718CB | ExxonMobil Chemical | mPE | Exceed™ |
| Karina IVORY PVC COMPOUND 807D35/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |