RIALFLAME H V0S 07 HW 30 G
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFLAME |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7h74Ql_RIALFLAME-H-V0S-07-HW-30-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-extinguishing homopolymer halogenated (UL-94: V-0) polypropylene compound 30% glass fiber reinforced. Stabilized for use in temperature and in contact with hot metallic parts. Excellent mechanical properties and flame reaction in a wide thermal range; indicated for injection molding of parts destined to electric-lighting sector. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.40 | % | |
| Ash Content | 30 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 16.7 | day | ISO 4577 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Needle Flame Test 1(2.00 mm) | Pass | IEC 60695-2-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 75.0 | MPa | ISO 527-2/20 |
| Tensile Strain (Break, 23°C) | 6.0 | % | ISO 527-2/20 |
| Flexural Modulus 2(23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 4.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature (2.00 mm) | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A-B |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PBB106 | Polyram Ram-On Industries | PC+ABS | RAMLLOY |
| Teflon® AF 1600 | DuPont Fluoropolymers | Fluoropolymer | Teflon® AF |
| Monprene® CP-19238 | Teknor Apex Company | TPE | Monprene® |
| TECACOMP® PBT TF natural 3438 | Ensinger GmbH | PBT | TECACOMP® |
| ULTEM™ 2310 resin | SABIC Innovative Plastics | PEI | ULTEM™ |