Tritan™ TX1801 Natural
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7gviGN_Tritan-TX1801-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ Copolyester TX1801 is an amorphous copolyester specifically developed for use in blow molding applications. Eastman Tritan™ Copolyester TX1801 contains a mold release derived from vegetable based sources. Its most outstanding features are excellent toughness, hydrolytic stability, heat resistance, and chemical resistance. In addition, this new generation copolyester offers excellent appearance and clarity. Eastman Tritan™ Copolyester TX1801 may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1610 | MPa | ASTM D638 |
| 23°C | 1570 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 45.0 | MPa | ASTM D638, ISO 527-2 |
| Fracture, 23°C | 52.0 | MPa | ASTM D638 |
| Fracture, 23°C | 51.0 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield, 23°C | 7.0 | % | ASTM D638, ISO 527-2 |
| Fracture, 23°C | 140 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1520 | MPa | ASTM D790 |
| 23°C | 1490 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 60.0 | MPa | ISO 178 |
| Yield, 23°C | 64.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D256 |
| -40°C | 12 | kJ/m² | ISO 180 |
| 23°C | 78 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Maximum Load | 67.0 | J | ASTM D3763 |
| 0°C, Energy at Maximum Load | 65.0 | J | ASTM D3763 |
| 23°C, Energy at Maximum Load | 62.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 101 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr |
| Injection instructions |
|---|
| ISBM Melt Temperature: 260 to 280°CISBM Injection Mold Temperature: 40 to 65°CISBM Blow Mold Temperature: 35 to 55°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr |
| Extrusion instructions |
|---|
| EBM Melt Temperature: 235 to 255°CEBM Blow Mold Temperature: 15 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® FFU50 | A. Schulman Europe | ABS | RONFALIN® |
| Versaflex™ OM 6160-1 | PolyOne Corporation | TPE | Versaflex™ |
| LEXAN™ HFR1724 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LUVOCOM® 1700-8126 | Lehmann & Voss & Co. | PPE | LUVOCOM® |
| POLYCOMPO PE 7800M | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |