VECTRA® S135
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7gOE2B_VECTRA-S135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
35% glass reinforced Vectra grade with very low outgassing, very high heat deflection temperature (335°C) and stiffness. Typical applications are lampsockets, lensholders for beamers, electrical and electronic parts like connectors, relays, switches, coil bobbins and also under the hood applications. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural at 0.28mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.40 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.0E-3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 7.0E-3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Flexural Strain at Break | 2.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 14 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 340 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 267 | °C | ISO 75-2/C |
| Melting Temperature 1 | 350 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 350 - 360 | °C | |
| Middle Temperature | 355 - 365 | °C | |
| Front Temperature | 360 - 370 | °C | |
| Nozzle Temperature | 370 - 380 | °C | |
| Processing (Melt) Temp | 370 - 380 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 360 to 370°CZone 4 Temperature: 365 to 375°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® FRGFT1741-BK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| KumhoSunny PC/ABS HAC8270HF | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina CLEAR PVC COMPOUND 80/229-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST ZK 6400WW30 | Ester Industries Ltd. | PC | ESTOPLAST ZK |
| Sylvin 4250-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |