Latilon 28D G/20
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7fAtGl_Latilon-28D-G-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polycarbonate (PC). Glass fibres. Product UL certified. Low smoke toxicity index and optical density. High dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.40 to 0.60 | % | |
| Flow : 2.00 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 5900 | MPa | |
| 60°C | 5300 | MPa | |
| 90°C | 4900 | MPa | |
| 120°C | 4800 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 85.0 | MPa | |
| Break, 60°C | 75.0 | MPa | |
| Break, 90°C | 60.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 1.9 | % | |
| Break, 90°C | 1.7 | % | |
| Break, 120°C | 1.6 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.5 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 30 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Oxygen Index | 31 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2900-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP2636 | LyondellBasell Industries | PP Homopolymer | Moplen |
| BLUESTAR® POM BS090A | Beijing Ranger Chemical Co., Ltd. | Acetal (POM) Copolymer | BLUESTAR® POM |
| LUBEMID A26 ER NATURAL | LUBEN PLAST srl | Nylon 66 | LUBEMID |
| Hifax CA60A NA 598F ANTHRACITE | LyondellBasell Industries | PP, Unspecified | Hifax |