Lupol® LW4405
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7eQbMz_Lupol-LW4405.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Low Warpage Application Electrical & Electronic, Automotive Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 85.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | < 10 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 7060 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 3.20 mm) | 155 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 4.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RALUPOL® UP 804 | RASCHIG GmbH | Polyester, TS | RALUPOL® |
| X-Pro PP 2315 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| ECOLEN® HF20M | HELLENIC PETROLEUM S.A. | PP Homopolymer | ECOLEN® |
| HiFill® PA6/6 GF8 IM4 HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LNP™ LUBRICOMP™ EX00548C compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |