LNP™ THERMOCOMP™ UX06032-WH9E041 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7byAGA_LNP-THERMOCOMP-UX06032-WH9E041-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UX06032 is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, Heat Stabilized. Custom color white. Also known as: LNP* THERMOCOMP* Compound UX06032-WH9E041 Product reorder name: UX06032-WH9E041 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 93.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 9600 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 265 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 825 | °C | |
| 1.60 mm | 825 | °C | |
| 3.00 mm | 850 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 295 to 315 | °C | |
| Processing (Melt) Temp | 305 to 315 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E380PKOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sylvin 8756-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Clariant Nylon 6/6 PA-111M40 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Hybrid S459 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Karina IVORY PVC COMPOUND 105551-35/1-Y-IS-SD-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |