DESLON™ 66 DSC214GM
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7bXSb6_DESLON-66-DSC214GM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC214GM is one of the brands which made by Polyamide66 that filled Glass Fiber/Mineral Filler 35% and reinforced goods. It provides high mechanical strength property, modification resistance, good surface appearance, thermal property. Applications: DESLON™ DSC201AG6 is one of the most-used for good mechanical property, dimensions stability and good abrasion resistance property goods, such as Bushing of Automotive parts, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 - 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6370 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 255 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 235 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 275 - 285 | °C | |
| Middle Temperature | 285 - 290 | °C | |
| Front Temperature | 285 - 295 | °C | |
| Nozzle Temperature | 285 - 295 | °C | |
| Processing (Melt) Temp | 285 - 295 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HIPOL™ J740 | Mitsui Chemicals, Inc. | PP Impact Copolymer | HIPOL™ |
| ICORENE® K1500 | ICO Polymers APAC, A Division of A. Schulman | XLPE | ICORENE® |
| Petrotene® PP A1 BRCA001 PH104 MSP | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| LNP™ LUBRICOMP™ DFL36E compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| ULTEM™ 2110R resin | SABIC Innovative Plastics | PEI | ULTEM™ |