MAJORIS G300BS
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7av7DW_MAJORIS-G300BS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS G300BS is a special long glass fibre reinforced bio polymer grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the bio polymer matrix, are providing with outstanding mechanical properties. APPLICATIONS MAJORIS G300BS is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS G300BS make it suitable for:
MAJORIS G300BS can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 101 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2/50 |
| Flexural Modulus | 5100 | MPa | ISO 178 |
| Flexural Stress 1 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 58 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 141 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10%Holding time: as long as practical |
| Note Message | |
|---|---|
| 1 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1F-4080 | Spartech Polycom | ABS | Spartech |
| AIE PA66 6010ST | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Boda BDF25CP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Anjacom® 050/75S | Almaak International GmbH | PC+ABS | Anjacom® |
| HiFill FR® ABS GB10 FR | Techmer Engineered Solutions | ABS | HiFill FR® |