PLEXIGLAS® Satinice df22 8N, based on PLEXIGLAS® 8N, is characterized by diffuse scattering of light.

Typical properties of PLEXIGLAS® molding compound are

good flow

high mechanical strength, surface hardness and mar resistance

very good weather resistance.

Special properties of PLEXIGLAS® Satinice df22 8N are

very good lightdiffusion combined with excellent light transmission.

Application:
Used for injection molding items for lighting engineering applications

Examples:
luminaire covers, projection screens and similar applications

General Information
Features	Good Flow Good Weather Resistance High Hardness High Strength Light Stabilized
Uses	Lighting Diffusers Video Equipment
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	2.40	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Stress (Break)	67.0	MPa	ISO 527-2/5
Tensile Strain (Break)	3.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	1.8	kJ/m²	ISO 179/1
Charpy Unnotched Impact Strength (23°C)	18	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	103	°C	ISO 75-2/B
1.8 MPa, Unannealed	98.0	°C	ISO 75-2/A
Glass Transition Temperature	110	°C	ISO 11357-2
Vicat Softening Temperature	109	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	6.3E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	700	°C	IEC 60695-2-13
Fire Rating	B2		DIN 4102

Additional Information	Nominal Value	Unit	Test Method
Half-Value Angle	12.5	°	DIN 5036

Optical	Nominal Value	Unit	Test Method
Transmittance ¹	86.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	< 95.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	60.0 to 90.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
BMC 100	Bulk Molding Compounds, Inc.	Polyester, TS	BMC
Cheng Yu T889G25	Cheng Yu Plastic Company Limited	PBT	Cheng Yu
Huafon HF-1380A	Huafon Group Co., Ltd.	TPU-Polyester	Huafon
KEBAFLEX® SG 55 A.01	BARLOG plastics GmbH	TES	KEBAFLEX®
TAFMER™ BL3110M	Mitsui Chemicals, Inc.	PAO	TAFMER™