RAMTAL PM1509
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTAL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7aXyF7_RAMTAL-PM1509.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYACETAL COPOLYMER FOR DECREASED FRICTION AND IMPROVED WEAR RESISTANCE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 - 2.2 | % | ASTM D955 |
| -- | 1.8 - 2.2 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.22 | % | ASTM D570 |
| Saturated, 23°C | 0.22 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 80 | ASTM D785 | |
| R scale | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 50 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 75.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C | 7.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.80 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 175 - 200 | °C | |
| Middle Temperature | 180 - 205 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Mold Temperature | 60.0 - 110 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan 2260/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| AKROMID® A3 GF 30 2 RM-D black (5388) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Alpha PVC AG K580D-N14A NATURAL | AlphaGary | PVC Elastomer | Alpha PVC |
| EcoLon® MRGF1619-BK3 | Wellman Engineering Resins | Nylon 66 | EcoLon® |
| POLYAXIS® PD 3000 | A. Schulman Inc. | PP Copolymer | POLYAXIS® |