Aplax P2213GN
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Aplax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7aQqKS_Aplax-P2213GN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aplax P2213GN is a 10 % talcum reinforced PP product for injection moulding in natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (1.60 mm) | 1.4 - 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 90 | % | ISO 527-2 |
| Flexural Modulus | 2070 | MPa | ISO 178 |
| Flexural Stress | 46.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 125 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | > 165 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1, notch 0.25in: 48 kg cm/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 220 | °C | |
| Middle Temperature | 170 - 220 | °C | |
| Front Temperature | 170 - 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 400 HI | RTP Company | PS (HIPS) | RTP |
| Moplen EP339R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Gallonprene® GP540-7501(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Ultramid® Structure B3WG12 LFX BK23215 | BASF Corporation | Nylon 6 | Ultramid® |
| NORYL™ GFN1 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |