LNP™ THERMOCOMP™ WX05502 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7W56MR_LNP-THERMOCOMP-WX05502-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* WX05502 is a compound based on Polyester, TP resin containing Flame Retardant, Glass Fiber, Mineral. Added features of this material include: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound 9750 Product reorder name: WX05502 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.81 | g/cm³ | |
| -- | 1.80 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13200 | MPa | ASTM D638 |
| -- | 11700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 90.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 1.3 | % | ISO 527-2/5 |
| Break 3 | 1.4 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 10900 | MPa | ASTM D790 |
| -- 5 | 11400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 142 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 19 | J/m | ASTM D256 |
| 23°C 7 | 4.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D4812 |
| 23°C 8 | 22 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.60 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 221 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 197 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 GB 30 | RTP Company | ABS | RTP |
| RTP 300 EM | RTP Company | PC | RTP |
| 3M™ Dyneon™ Fluoroplastic PFA 6503PAZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| Andur AL 80-5 AP-FP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Petrotene® PP A3 G24 T8 NTLA010 PH345 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |