PrimoPrene 87A-1000

Category:	TPV , Thermoplastic Vulcanizate
Manufacturer:	KMI Group Inc.
Trademark:	PrimoPrene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7UvRTp_PrimoPrene-87A-1000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Attributes:

PrimoPrene TPV is a thermoplastic elastomer containing fully vulcanized EPDM rubber.

It is ideal solution for applications requiring long term sealing performance even at elevated temperatures up to 135°C (275F).

Soft-touch feel for grips and handles used in automotive and consumer goods.

Can be processed using conventional thermoplastic processing equipment.

There is no need for costly and energy guzzlind down stream equipment for curing.

Suitable for injection molding, blow molding, profile and sheet extrusion applications.

PrimoPrene TPV is supplied in weatherable (UV Stabilized) black.

Applications:
PrimoPrene is a cost effective solution for replacing Santoprene rubber, styrenic-based TPEs, and thermoset rubbers such as EPDM, and Polychloroprene. It is an excellent choice for applications requiring flexibility in the following markets: automotive parts, appliance, business machines, construction, consumer products, and electronics.

General Information
Additive	Rubber 2 UV Stabilizer
Features	Good Colorability Good Flexibility Good Heat Seal Good UV Resistance Soft
Uses	Appliances Automotive Applications Business Equipment Construction Applications Consumer Applications Electrical/Electronic Applications Flexible Grips Handles
Appearance	Black
Processing Method	Blow Molding Extrusion Injection Molding Profile Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.960	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) ¹(230°C/10.0 kg)	10 to 18	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness			ASTM D2240
Shore A, 5 sec	87
Shore A, 15 sec	85

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ²(100% Strain, 23°C)	6.20	MPa	ASTM D412
Tensile Strength ³(Yield, 23°C)	16.2	MPa	ASTM D412
Tensile Elongation ⁴(Break, 23°C)	540	%	ASTM D412
Tear Strength ⁵(23°C)	60.0	kN/m	ASTM D624
Compression Set			ASTM D395
70°C, 22 hr	41	%
125°C, 70 hr	72	%

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-60.0	°C	ASTM D746
Melting Temperature	159	°C

Additional Information	Nominal Value		Test Method
Ozone Resistance ⁶	Excellent		ASTM D1149

Injection	Nominal Value	Unit
Drying Temperature	82.2	°C
Drying Time	3.0	hr

Extrusion	Nominal Value	Unit
Drying Temperature	65.6	°C
Drying Time	3.0	hr

Note Message
1 .	Procedure A
2 .	500 mm/min
3 .	500 mm/min
4 .	500 mm/min
5 .	Die C, 500 mm/min
6 .	500 hr, 100 pphm O3 conc.

Resin Grade	Manufacturer	Category	Trademark
PRIMATOP HDPE 006964	Amco Polymers	HDPE	PRIMATOP
Resinoid 1345	Resinoid Engineering Corporation	Phenolic	Resinoid
Viprene™ G45D-32U-NAT	Alliance Polymers & Services	TPV	Viprene™
FERREX® GPP20CF54UL-WH	Ferro Corporation	PP, Unspecified	FERREX®
FRIANYL® A3 V0	Nilit Plastics	Nylon 66	FRIANYL®