FARBOSET® 1115
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Cosmic Plastics, Inc. |
| Trademark: | FARBOSET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Uttil_FARBOSET-1115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cosmic FARBOSET 1115 Black is a mineral filled epoxy molding compound featuring fast cure rates, and excellent hot strength. It is designed for the encapsulation of coils, transformers, bushings, switches and other electrical and electronic components requiring good hot rigidity in molding. This material is used extensively in injection and transfer molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1 | 2.04 | g/cm³ | |
| Apparent Density 2 | 1.00 | g/cm³ | |
| Spiral Flow | 71.0 | cm | |
| Molding Shrinkage - Flow | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.026 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 97 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 86.2 | MPa | |
| Flexural Modulus | 17200 | MPa | |
| Flexural Strength | 124 | MPa | |
| Compressive Strength | 276 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | |
| Glass Transition Temperature | 130 | °C | |
| CLTE - Flow | |||
| -- 3 | 3.2E-5 | cm/cm/°C | |
| -- 4 | 8.7E-5 | cm/cm/°C | |
| Thermal Conductivity | 1.3 | W/m/K | |
| Maximum Operating Temperature - Intermittent | 200 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Loss Factor - 1 kHz | 0.0320 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | |
| Volume Resistivity | > 5.0E+16 | ohms·cm | |
| Dielectric Strength 5(3.18 mm) | > 16 | kV/mm | |
| Dielectric Constant (1 kHz) | 4.50 | ||
| Dissipation Factor (1 kHz) | 7.0E-3 | ||
| Arc Resistance | 180 | sec |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 6 | |||
| 5°C | 52 | wk | |
| 25°C | 1.0 | wk | |
| 35°C | 0.29 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time | |||
| 150°C 7 | 8.3E-3 | hr | |
| 150°C | 0.017 to 0.050 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 150 to 180 | °C | |
| Injection Pressure | 0.345 to 6.89 | MPa |
| Note Message | |
|---|---|
| 1 . | Molded |
| 2 . | Powder |
| 3 . | Alpha 1 |
| 4 . | Alpha 2 |
| 5 . | Method A (Short-Time) |
| 6 . | Defined as not more than 40% loss of spiral flow based on original values. |
| 7 . | Hot Plate Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 1480 N | RTP Company | PESU | RTP |
| Spartech Polycom X02475 | Spartech Polycom | PP Homopolymer | Spartech |
| ELASTOSIL® RT 426 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Pebax® HD 6313 SP 01 | Arkema | PEBA-Ether | Pebax® |
| LNP™ LUBRILOY™ R2000 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |