Axiall PVC SP-7107
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7UGedi_Axiall-PVC-SP-7107.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Georgia Gulf SP-7107 is a general purpose, electrical grade rigid vinyl injection molding compound characterized by excellent flow, heat stability, color hold, and surface appearance. This makes it an ideal choice for applications such as electrical outlet boxes, terminal strip housings, and appliance parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2620 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.18 mm | 59 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 800 | J/m | ASTM D256 |
| Dart Drop Impact (23°C, 12.7 mm) | 20.8 | J | ASTM D3029 |
| Drop Impact Resistance (23°C) | 129 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 74.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| RTI Elec (1.40 mm) | 90.0 | °C | UL 746 |
| RTI Imp (1.40 mm) | 85.0 | °C | UL 746 |
| RTI (1.40 mm) | 90.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 5VA | UL 94 | |
| Oxygen Index | 36 | % | ASTM D2863 |
| Additional Information |
|---|
| UL Flame Spread Index, ASTM-E162: RP-42Flow Ratio, Georgia Gulf Test, Distance/Wall Thickness, 390-400°F: 215 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Shot Size | 35 - 75 | % | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 163 | °C | |
| Middle Temperature | 174 - 191 | °C | |
| Front Temperature | 182 - 193 | °C | |
| Nozzle Temperature | 177 - 193 | °C | |
| Processing (Melt) Temp | 202 - 210 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 82.7 - 138 | MPa | |
| Holding Pressure | 48.3 - 82.7 | MPa | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 25 - 80 | rpm | |
| Clamp Tonnage | 3.4 | kN/cm² | |
| Screw L/D Ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 3500-85A | Vi-Chem Corporation | TPE | Sevrene® |
| SynPlast™ DUP-E | PolyOne Corporation | Di Undecyl Phthalate | SynPlast™ |
| Cheng Yu PP225 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Electrafil® ABS CF15 BK | Techmer Engineered Solutions | ABS | Electrafil® |
| POLYFORT® AFP 3318 | A. Schulman Europe | PP Copolymer | POLYFORT® |