Shinko-Lac® ABS GH-8
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7TY7sL_Shinko-Lac-ABS-GH-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS GH-8 is a standard grade of ABS that features ultra-high impact resistance along with an excellent balance of rigidity, strength, processability and glossiness. Typical applications of GH-8 include shoe heels, safety helmets and air conditioner accessories. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 35.3 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 53.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 150 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 280 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 89.0 | °C | ASTM D648 |
| CLTE - Flow | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN RX-13000 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| ABSCOM® FR1000 | Polymer Compounders Limited | ABS | ABSCOM® |
| Elastron® G G100.D43.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Kingfa HR-528 | Kingfa | ABS | Kingfa |
| Sylvin 9600-55 Green 3108 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |