LEXAN™ BFL4000U resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7TT13u_LEXAN-BFL4000U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed for high light reflectance and light shielding applications with good UV weathering capability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2240 | MPa | ASTM D638 |
| -- | 2040 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/5 |
| Break 3 | 47.0 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 5 | 56 | % | ASTM D638 |
| Break | 74 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2050 | MPa | ASTM D790 |
| -- 7 | 2170 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 83.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 30 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 240 | J/m | ASTM D256 |
| 23°C | 470 | J/m | ASTM D256 |
| -30°C 10 | 20 | kJ/m² | ISO 180/1A |
| 23°C 11 | 30 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 68.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 134 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 115 | °C | ISO 75-2/Af |
| 1.8 MPa, Annealed, 3.20 mm | 115 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ASTM D1525 14 |
| -- | 137 | °C | ISO 306/B50 |
| -- | 139 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 260 to 282 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TPSF-FRG30 | Polymer Resources Ltd. | PBT | PRL |
| Starex VE-1801 | SAMSUNG SDI CO., LTD. | PS (HIPS) | Starex |
| Ultradur® B 4300 G4 LS High Speed BK15045 | BASF Corporation | PBT | Ultradur® |
| SQUARE® SSR1502-40 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |
| ESTOPLAST XU 230BB11 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |