BESTNYL SE25VI02AHC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7T4sCt_BESTNYL-SE25VI02AHC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 black with 25% glass fibre reinforcement and heat stabilized with good finish surface generally used for pieces wich aesthetic application and good mechanical properties in conjunction with good injection behaviour, for general and automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Ash Content | 25 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2 |
| Tensile Stress | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 275 to 285 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-40A | RTP Company | TPV | RTP |
| Starflam AFR450B | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| DJSilicone NE--D-1/NE-D-1U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Lucene™ LC168 | LG Chem Ltd. | TPO (POE) | Lucene™ |
| POLYBEST 6 PD GF30 natural | POLYMA Kunststoff GmbH & Co. KG | Nylon 6 | POLYBEST |