SLOVAMID® 66 SHI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Rnf01_SLOVAMID-66-SHI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified reactive thermoplastic rubber, moldings designed for high toughness even at low temperatures. Appropriate use of ski boots, helmets for sports and other security applications / hockey, building /, car door moldings, bear high dynamic stresses up to - 40°C. Supplied in natural finish and a range of RAL color scale. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 1.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.8 | % | |
| Flow | 1.8 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 950 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 50 | % | ISO 527-2 |
| Flexural Modulus | 800 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 45 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 43.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Elastollan® 1195A10LC | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Hostaform® CP15X | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| INEOS PP N12N-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| LNP™ FARADEX™ ES003E compound | SABIC Innovative Plastics | PEI | LNP™ FARADEX™ |
| AXLENE® 20 | INDELPRO, S.A. de C.V. | PP Homopolymer | AXLENE® |