TechnoPet: Attractive and cost effective

The TechnoPet compound line contains non-reinforced, glass fiber reinforced, impact strength modified as well as UV stabilized compounds for outdoor use.

TechnoPet compounds offer these properties:

High stiffness

High thermal stability >220°C

Attractive surface

High dimensional stability

For these reasons they represent an extremely cost effective solution compared with other technical compounds.

Typical Applications

Automotive industry: e.g. as a substitute for PA, engine covers...

Electrical engineering: e.g. lamp holders: glass fiber reinforced, flame retardant, high stiffness; multiple power sockets: modified impact strength, high dimensional accuracy...

Household appliances: e.g. steam irons: thermally stabilized PET compounds...

Packaging/logistics: e.g. logistic systems: modified impact strength, structural stability and strength...

Mechanical engineering: castors, bearings, gears, guide slide bearings...

General Information
Filler / Reinforcement	Glass fiber reinforced material, 45% filler by weight
Features	High Dimensional Stability Rigidity, high Insulation Thermal stability, good Good appearance
Uses	Packaging Gear Electrical/Electronic Applications Electrical appliances Application in Automobile Field Bearing

Physical	Nominal Value	Unit	Test Method
Density	1.73	g/cm³	ISO 1183
Molding Shrinkage ¹			ISO 2577
Transverse flow	1.0	%	ISO 2577
Flow	0.25	%	ISO 2577
Water Absorption			ISO 62
23°C, 24 hr	0.15	%	ISO 62
Saturated, 23°C	0.40	%	ISO 62
Viscosity Number (Reduced Viscosity)	58.0	ml/g	ISO 1628

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness ²	260	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17000	MPa	ISO 527-2/1
Tensile Stress (Break)	175	MPa	ISO 527-2/5
Tensile Strain (Break)	1.5	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	10	kJ/m²	ISO 179/1eA
23°C	10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	35	kJ/m²	ISO 179/1eU
23°C	35	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	210	°C	ISO 75-2/A
8.0 MPa, not annealed	145	°C	ISO 75-2/C
Vicat Softening Temperature	240	°C	ISO 306/B50
Melting Temperature ³	240	°C	ISO 11357-3
CLTE - Flow (23 to 80°C)	1.5E-5	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+14	ohms	IEC 60093
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (1.00 mm)	31	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	4.80		IEC 60250
1 MHz	4.20		IEC 60250
Comparative Tracking Index (Solution A)	250	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.8 mm)	HB		UL 94
Glow Wire Flammability Index (2.0 mm)	750	°C	IEC 60695-2-12

Note Message
1 .	275°C / WZ 135 bzw. 100°C, 600 bar
2 .	358 N
3 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
SABIC® Vestolen A RELY 5922R 10000	Saudi Basic Industries Corporation (SABIC)	HDPE	SABIC® Vestolen A
Nanjing Hongrui PP P830	Nanjing Hongrui Engineering Plastics Co., Ltd.	PP, Unspecified	Nanjing Hongrui PP
AIE PC 10G4	Asia International Enterprise (Hong Kong) Limited	PC	AIE PC
KUBE PIR 22302	KUBE Electronics AG	HDPE	KUBE PIR
Idemitsu PS HT50	Idemitsu PS	PS (GPPS)	Idemitsu PS