Pibiter® NRV30 NAT001
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiter® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Qit9E_Pibiter-NRV30-NAT001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced PBT grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.35 | % | Internal Method |
| Water Absorption | |||
| 23°C, 24 hr | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Ash Content | 30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ASTM D638 |
| Tensile Strength (Break) | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 9000 | MPa | ASTM D790 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| Vicat Softening Temperature | 215 | °C | ASTM D1525 1 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 3.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 235 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 260 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 505 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Quadrant EPP HDPE Black | Quadrant Engineering Plastic Products | HDPE | Quadrant EPP |
| Retpol® 3013 HS UV3 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| TIPPLEN® R 159 A | TVK Plc. (Tiszai Vegyi Kombinát) | PP Random Copolymer | TIPPLEN® |
| Gallonprene® GP640-9501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |