Smoothblend® POM-1201
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Smoothblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7PYTVA_Smoothblend-POM-1201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Smoothblend® POM-1201 is a wear resistance polyacetal compound offering superb lubricity and high mechanical and thermal properties by incorporating PTFE and glass fiber. It is developed for applications demanding stringent wear resistant and low friction performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4080 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.45 | ||
| vs. Steel - Static | 0.40 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 145 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 185 | °C | |
| Middle Temperature | 185 to 190 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 200 to 210 | °C | |
| Processing (Melt) Temp | 185 to 215 | °C | |
| Mold Temperature | 80.0 to 105 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP513 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| Tuftec™ H1062 | AKelastomers | SEBS | Tuftec™ |
| NEOFLON™ NP-20 | DAIKIN AMERICA, INC. | FEP | NEOFLON™ |
| Nipol® NBR DN219 | Zeon Corporation | NBR | Nipol® NBR |