LNP™ LUBRICOMP™ RL003 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Ony0E_LNP-LUBRICOMP-RL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RL003 is a compound based on Nylon 66 resin containing 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4030 Product reorder name: RL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Across Flow : 24 hr | 1.0 to 3.0 | % | ASTM D955 |
| Flow : 24 hr | 1.0 to 3.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 73.8 | MPa | ASTM D638 |
| Break | 73.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 11 | % | ASTM D638 |
| Break | 8.9 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 90.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.32 | ||
| vs. Itself - Static | 0.30 | ||
| Wear Factor - Washer | 28.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 33 | J/m | ASTM D256 |
| 23°C 1 | 4.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1000 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 64.0 mm Span) | 82.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime ABS Weather-X 100 | Primex Plastics Corporation | ABS+Acrylic | Prime ABS Weather-X |
| Shanghai Potomer N-500 | Shanghai Potomer International Trade Co., Ltd. | CPVC | Shanghai Potomer |
| Fusabond® C190 | DuPont Packaging & Industrial Polymers | EVA | Fusabond® |
| ECOGRAN® PEHDI BLEU | Eurocompound Polymers | HDPE | ECOGRAN® |
| Sylvin 9077-90C BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |