Hiprolon® 200 MNWHL G30
| Category: | Nylon 1010 , Polyamide 1010 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7OdADp_Hiprolon-200-MNWHL-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hiprolon® 200 MNWHL G30 is a polyamide 10.10 produced from a renewable source and reinforced with 30% glass fiber. This black grade is designed for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow | 0.70 | % | ISO 2577, ISO 294-4 |
| Flow | 0.20 | % | ISO 294-4, ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 136 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 95 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 190 | °C | ISO 306 |
| Melting Temperature | 202 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 1010, MHLR, 22-070, GF 30 | ISO 1874 | |
| Renewable Carbon Conent | > 95 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E General Purpose G-2184 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E General Purpose |
| Sylvin 2910-93 Green 3170 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Zytel® 132F NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| ADMER™ AT1707E | Mitsui Chemicals Europe GmbH | LLDPE | ADMER™ |
| Boda BDP-H9701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |