SUMIKON® PM-6600 Type Black is a Short Glass fiber & Mineral molding compound based on Phenolic Novolac polymer. It is supplied in the form of Granular/Molding Powder for Molding. |
General Information | |
---|---|
Filler / Reinforcement |
|
Appearance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.79 | g/cm³ | JIS K6911 |
Molding Shrinkage - Flow | 0.22 | % | JIS K6911 |
Water Absorption (Equilibrium) | 0.060 | % | JIS K6911 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength | 110 | MPa | JIS K6911 |
Flexural Modulus | 15300 | MPa | JIS K6911 |
Flexural Strength | 210 | MPa | JIS K6911 |
Compressive Strength | 260 | MPa | JIS K6911 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | 5.1 | kJ/m² | JIS K6911 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 208 | °C | JIS K6911 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Dielectric Strength 1 | 16 | kV/mm | JIS K6911 |
Insulation Resistance | JIS K6911 | ||
-- 2 | 1.0E+12 | ohms | JIS K6911 |
-- 3 | 5.0E+11 | ohms | JIS K6911 |
Note Message | |
---|---|
1 . | Method B (step by step) |
2 . | As molded |
3 . | After boiling |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 1200 T-70A UV | RTP Company | TPU-Polyether | RTP |
RTP 4007 SI 1 | RTP Company | PPA | RTP |
AKROMID® S3 GF 15 1 natural (3223) | AKRO-PLASTIC GmbH | Nylon 610 | AKROMID® |
Electrafil® PA6 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
LNP™ THERMOCOMP™ UFW49S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |