| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | POPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7NsWk8_POPELEN-HSP-375.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Low Density, Anti Scratch |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 1960 | MPa | ASTM D790 |
| Flexural Strength | 37.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C | 59 | J/m | |
| 23°C | 150 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200E SI 2 | RTP Company | Nylon, Unspecified | RTP |
| NOVALAC RX®626 | Vyncolit N.V. | Phenolic | NOVALAC |
| CGPC PVC H-73 | China General Plastics Corporation | PVC, Unspecified | CGPC PVC |
| POLYFLAM® RPP 1058X | A. Schulman Inc. | PP, Unspecified | POLYFLAM® |
| Dynalloy™ GP 7810-70T | PolyOne Corporation | TPE | Dynalloy™ |