Polimid A 25 GF V0F
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Poliblend S.p.a. |
| Trademark: | Polimid A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7NLAcB_Polimid-A-25-GF-V0F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polimid A 25 GF V0F is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Important attributes of Polimid A 25 GF V0F are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 125 | MPa | |
| Break | 125 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.5 | % | |
| Break | 4.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 110 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/A120 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Without Load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFT33N051-NBK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Niretan B F10 | Soredi S.p.a. | Nylon 6 | Niretan B |
| NORYL™ EXNL0143 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| KOPA® KN333NW | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Braskem PE HDB0355 | Braskem IDESA | HDPE | Braskem PE |