RTP 300 TFE 15 SI
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7NDsXk_RTP-300-TFE-15-SI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 300 TFE 15 SI is an unreinforced PTFE/silicone lubricated polycarbonate. It exhibits low wear and low frictional characteristics while maintaining the inherent toughness of the polycarbonate. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1930 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.5 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 79.3 | MPa | ASTM D790 |
| Compressive Strength | 68.9 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.10 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1900 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.010 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, RTP Tested) | V-0 | UL 94 |
| Additional Information |
|---|
| Molding shrinkage, Linear-flow, ASTM D955, 0.25in: 8mil/inThe coefficient of friction was tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 288 - 343 | °C | |
| Middle Temperature | 288 - 343 | °C | |
| Front Temperature | 288 - 343 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551000-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Stylac™ R440T | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| WPP PP JOSB26624 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Exxtral™ Performance Polyolefin CNU017 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| LNP™ LUBRICOMP™ LX92134 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |