NOVAPOL® PF-Y821-KPR
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7MnBfc_NOVAPOL-PF-Y821-KPR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL®PF-Y821-KPR is a linear low density polyethylene material,. This product is available in North America and is processed by film extrusion or blow molding. NOVAPOL®The main features of the PF-Y821-KPR are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | < 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 190 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 230 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 660 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 200 | g | ASTM D1922 |
| TD : 38 µm, blown film | 390 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 57 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture 2(38.0 µm) | 320 | J/cm | Internal method |
| Film properties are typical of blown film extruded at a blowup ratio of 2.5:1; but are dependant upon operating conditions. |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermx® TE4004 | Celanese Corporation | PCT | Thermx® |
| Hostacom TKC 151N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| Sylvin 83012-90UV Grey 9363 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LUVOCOM® 1850-7692/BK VP | LEHVOSS Group | PBT | LUVOCOM® |
| Sylvin 2910-50 Blue 8383 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |