PENTAMID AB S L5 H1 natural
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Lo7Yx_PENTAMIDABSL5H1natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity, high heat stabilised polyamide 66+6,easy flow, very easy moulding, impact modifed |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.4 | % | ISO 294-4 |
| Flow | 1.4 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 8.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.6 | % | ISO 62 |
| Viscosity Number | 120 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.3 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA66+PA6, MHR, 12-030 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.18 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 255 - 275 | °C | |
| Middle Temperature | 260 - 285 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 50.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Valtra® EA3300 | Saudi Polymers Company | PS (GPPS) | Valtra® |
| DENKA Transparent Polymer TE-30S | Denka Company Limited | ABS | DENKA Transparent Polymer |
| FRblend® PBT-1307 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| INSPIRE™ 702 | Braskem Europe GmbH | PP, Unspecified | INSPIRE™ |
| Karina IVORY PVC COMP. -E 105908-35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |