Sasol Polymers PE LT079
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Sasol Polymers |
| Trademark: | Sasol Polymers PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7LRSkp_Sasol-Polymers-PE-LT079.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With itself-dynamic, blown film | 0.41 | ASTM D1894 | |
| With itself-static, blown film | 0.42 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 430 | % | ASTM D882 |
| TD : Yield, 50 µm, blown film | 570 | % | ASTM D882 |
| Dart Drop Impact 1(50 µm, Blown Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 5.0 | g | ASTM D1922 |
| TD : 50 µm, blown film | 5.0 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 60 | ASTM D2457 | |
| Clarity | 40.0 | ASTM D1746 | |
| Haze | 7.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | g | ASTM D3354 | |
| The above values were measured on 50µm film produced on a 65mm Macchi extruder with Macchi LDPE screw and a 250mm die, using 208°C melt temperature, 610mm FLH, 2.5:1 blow ratio and a die gap of 0.8mm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 130 - 150 | °C | |
| Cylinder Zone 1 Temp. | 140 - 155 | °C | |
| Cylinder Zone 2 Temp. | 150 - 165 | °C | |
| Cylinder Zone 3 Temp. | 155 - 175 | °C | |
| Cylinder Zone 4 Temp. | 165 - 180 | °C | |
| Melt Temperature | 190 - 210 | °C | |
| Die Temperature | 170 - 180 | °C |
| Extrusion instructions |
|---|
| Should be processed on a conventional LDPE extruder, but can be processed on a LLDPE extruder (wide die gap) with drawdown limitations, inferior mechanical and film shrinkage properties. Recommended screen pack: 60/100/60 BS mesh. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Sinvicomp SIC3711 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| CALP 4300G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| DOMAMID® 6G30FC | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| ULTEM™ ATX200F resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |