MAJORIS AG100E
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7H9z6c_MAJORIS-AG100E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS AG100E is a 10% glass fibre reinforced polyethylene high density compound intended for injection moulding and extrusion profiles. The product is available in black (MAJORIS AG100E - 8229) and natural (MAJORIS AG100E) but other colours can be provided on request. APPLICATIONS MAJORIS AG100E is intended for components which require good impact strength, rigidity, dimensional stability. Suitable applications are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 18 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.60 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction : 2.00mm | 0.90 | % | |
| Flow direction : 2.00mm | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1490 | MPa | ISO 178 |
| Flexural Stress | 47.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 200 - 220 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4110G20 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Novalloy-A A5736 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |
| Chemical Resources HD3954ST | Chemical Resources, Inc. | HDPE | Chemical Resources |
| HAIPLEN EP50 T2 X2 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Sylvin 8200-88 Orange 5104 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |