BMC 200
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Bulk Molding Compounds, Inc. |
| Trademark: | BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7GxIc4_BMC-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BMC 200 is a high strength, low shrink molding compound. It can be supplied in bulk or extruded in pre-weighted slugs. Typical applications are circuit breakers, insulators, bobbins, electrical connectors and power tool housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.85 to 1.95 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0E-4 to 4.0E-4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 to 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 40 to 50 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.6 to 41.4 | MPa | ASTM D638 |
| Flexural Modulus | 12400 to 13800 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.9 to 103 | MPa | ASTM D790 |
| Compressive Strength | 124 to 138 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 to 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 15 to 17 | kV/mm | |
| -- 2 | 14 to 15 | kV/mm | |
| Arc Resistance (1.59 mm) | > 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (1.59 mm) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 138 to 166 | °C | |
| Middle Temperature | 138 to 166 | °C | |
| Front Temperature | 138 to 166 | °C | |
| Mold Temperature | 138 to 166 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| 2 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1302 TFE 20 | RTP Company | PPS | RTP |
| ALCOM® LD2 PC 1000 14008 WT1010-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LD2 PC |
| Flexalloy® 09-U0373R-80NT1 | Teknor Apex Company | PVC, Flexible | Flexalloy® |
| Karina BLUE PVC COMPOUND 950-06/554-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TABOREN® PH 41 G 30-095 | SILON s.r.o. | PP Homopolymer | TABOREN® |