Sarlink® TPE ME-2690B
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Gpsoz_Sarlink-TPE-ME-2690B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink ME-2690B is a high flow, high hardness molding grade with UV resistance, for automotive exterior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 5 seconds, injection molding | 95 | ISO 868 | |
| Shore D, 5 seconds, injection molding | 34 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain) | 7.30 | MPa | ISO 37 |
| Tensile Strength - Across Flow (Break) | 14.8 | MPa | ISO 37 |
| Tensile Elongation - Across Flow (Break) | 700 | % | ISO 37 |
| Compression Set (70°C, 22 hr) | 78 | % | ISO 815 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/s (200°C) | 160 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 10.0 - 60.0 | °C | |
| Injection Pressure | 6.00 - 12.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 4.00 - 6.00 | MPa | |
| Back Pressure | 0.500 - 2.00 | MPa | |
| Screw Speed | 50 - 120 | rpm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets 2 to 4 hours at 65 degrees Celsius.Time SettingsInjection Time: 0.5-2 secondsHolding Time: 1-10 secondsCooling Time: As short as possible. The parts should be removable without deformation or piercing of the ejector(s) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILAC® ABS-TR558-CL | Polymer Technology and Services, LLC | ABS | TRILAC® |
| ACCUTECH鈩?HP0339C40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| POLIMAXX 1102H | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| Rotuba CAB B9004 (22% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| Sylvin 5132-86 Clear Blue 8281 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |