Techsil 1387 BLACK
| Category: | Silicone , Silicone |
| Manufacturer: | Techsil Limited |
| Trademark: | Techsil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Gla6E_Techsil-1387-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Techsil 1387 is a fast cure 1-part RTV silicone sealant specially formulated for applications requiring a combination of good adhesion, excellent physical and non-corrosive properties. The Oxime based cure system produces excellent physical properties and good adhesion particularly to plastics and many other substrates. Although not totally neutral the cured sealant is very low corrosive in nature. Key Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | BS 903 |
| Molding Shrinkage - Flow | < 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 24 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 0.320 | MPa | BS 903 |
| Tensile Strength 2(Yield) | 1.90 | MPa | BS 903 |
| Tensile Elongation 3(Break) | 390 | % | BS 903 |
| Tear Strength 4 | 3.10 | kN/m | BS 903 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE | |||
| Flow | 2.8E-4 | cm/cm/°C | |
| Transverse | 8.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | |
| Service Temperature 5 | -50 to 275 | °C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Tack Free Time 6(23°C) | 13.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time 7(23°C, 3.00 mm) | < 1.0 | day | |
| Extrusion Rate | 860 | g/min | |
| Young's Modulus 8 | 0.550 | MPa |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.010 | ASTM D150 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity | 23500 | cP |
| Note Message | |
|---|---|
| 1 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 2 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 3 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 4 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 5 . | AFS 1540B |
| 6 . | 65%RH |
| 7 . | 65%RH |
| 8 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 MS 2 | RTP Company | Nylon 66 | RTP |
| Cellophane™ 500P | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| LNP™ COLORCOMP™ HF1110RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| Sylvin 9077-85 Blue 8363 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTOPLAST SR 1500GY01 | Ester Industries Ltd. | ABS | ESTOPLAST SR |