LACEA® H-100J (Unstretched) Datasheet,PLA,Mitsui Chemicals, Inc.-SHANGHAI SUSHENG

Message
LACEA®H-100J (Unstretched) is a polylactic acid (PLA) material,. This product is available in the Asia-Pacific region and is processed by blow molding or injection molding. LACEA®The main characteristics of H-100J (Unstretched) are: environmental protection/green. Typical application areas include: bag/lining packing Movie container non-woven fabric

General Information
Features	Biodegradable
Uses	Packaging Films Bags Container Non-woven fabric
Appearance	Clear/transparent
Forms	Particle
Processing Method	Blow film Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.26	g/cm³	ASTM D1505

Hardness	Nominal Value	Test Method
Rockwell Hardness		ASTM D785
L scale	84	ASTM D785
Class r	115	ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	68.0	MPa	ASTM D638
Tensile Elongation (Yield)	4.0	%	ASTM D638
Flexural Modulus	3700	MPa	ASTM D790
Flexural Strength	98.0	MPa	ASTM D790

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	250	µm
Secant Modulus - MD	2000	MPa	ASTM D882
Tensile Strength - MD (Yield)	70.0	MPa	ASTM D882
Tensile Elongation - MD (Break)	5.0	%	ASTM D882
Oxygen Permeability	60	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission	30	g/m²/24 hr	ASTM E96

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	29	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	55.0	°C	ASTM D648
Vicat Softening Temperature	58.0	°C	ASTM D1525

Additional Information
The value listed as Oxygen Permeability, ASTM D3985, was tested in accordance with JIS-K7126.The value listed as Water Vapor Transmission, ASTM E96, was tested in accordance with JIS-K7129.The value listed as Density, ASTM D1505, was tested in accordance with JIS-K6758.The value listed as Tensile Strength @ Yld MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Elongation @ Break MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Secant Modulus MD, ASTM D882, was tested in accordance with JIS-C2318.Oxygen Permeability, JIS-K7126. 23°C, Method A: 60 cm³/m²/day/atmNitrogen Permeability, JIS-K7126. 23°C, Method A: 4 cm³/m²/day/atmCO2 Permeability, JIS-K7126. 23°C, Method A: 120 cm³/m²/day/atm

Additional Information

The value listed as Oxygen Permeability, ASTM D3985, was tested in accordance with JIS-K7126.The value listed as Water Vapor Transmission, ASTM E96, was tested in accordance with JIS-K7129.The value listed as Density, ASTM D1505, was tested in accordance with JIS-K6758.The value listed as Tensile Strength @ Yld MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Elongation @ Break MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Secant Modulus MD, ASTM D882, was tested in accordance with JIS-C2318.Oxygen Permeability, JIS-K7126. 23°C, Method A: 60 cm³/m²/day/atmNitrogen Permeability, JIS-K7126. 23°C, Method A: 4 cm³/m²/day/atmCO2 Permeability, JIS-K7126. 23°C, Method A: 120 cm³/m²/day/atm

Injection	Nominal Value	Unit
Rear Temperature	150 - 160	°C
Middle Temperature	160 - 180	°C
Front Temperature	170 - 190	°C
Nozzle Temperature	160 - 180	°C
Mold Temperature	20.0 - 30.0	°C

Injection instructions
Cooling Time: 30 to 40 sec

Category:	PLA , Polylactic Acid
Manufacturer:	Mitsui Chemicals, Inc.
Trademark:	LACEA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7GEzZk_LACEA-H-100J-Unstretched-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Amilan® CM1012G-45N	Toray Resin Company	Nylon 6	Amilan®
GAPEX® RPP10EU28GY	Ferro Corporation	PP, Unspecified	GAPEX®
Generic Nylon 6 - Unspecified	Generic	Nylon 6	Generic
IDI BMC B20 (Glass Content 8%)	IDI Composites International	TS, Unspecified	IDI BMC
Polygen SG8R-BK	Shanghai Polygen Science and Technology Co., Ltd.	PPS	Polygen