Borlink™ LE0310-04
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7G871N_Borlink-LE0310-04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Borlink LE0310-04 is a crosslinkable black polyethylene compound, specially designed for semiconductive strippable insulation shield of energy cables. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D1928, ASTM D1505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | 1.8 | kN/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (121°C, 168 hr) | > 25 | % | ASTM D638 |
| Change in Ultimate Elongation in Air (121°C, 168 hr) | > 100 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -35.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D991 | ||
| 23°C | < 30 | ohms·cm | ASTM D991 |
| 90°C | < 1.0E+2 | ohms·cm | ASTM D991 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 115 - 125 | °C |
| Extrusion instructions |
|---|
| Hopper Drying (4 h) 40°C |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP1B30 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Tenac™ FS410 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Vi-Chem PVC V142-89 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Ultradur® B 4300 G2 High Speed | BASF Corporation | PBT | Ultradur® |
| Karina CLEAR PVC COMPOUND -E 75/232-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |