SABIC® PPcompound 55T1040
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7Fhxdx_SABIC-PPcompound-55T1040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 55T1040 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact and high rigidity, and is suitable for injection molding applications. The IMDS ID is 278629571 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2460 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 20.0 | MPa | ISO 527-2/50 |
| Break | 14.8 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | |
| Break | 11 | % | |
| Flexural Modulus 1(64.0 mm Span) | 3280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 2.0 | kJ/m² | |
| 23°C 3 | 8.2 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 2.7 | kJ/m² | |
| 23°C | 7.9 | kJ/m² | |
| Instrumented Dart Impact 5(23°C, Energy at Peak Load) | 10.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 70.4 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/A50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 2.20 m/sec |
| 6 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 572E3720012, Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| 4PET® 9L32320 HL | 4Plas | PET | 4PET® |
| POLYfill PP HBK30030 | Polykemi AB | PP Homopolymer | POLYfill |
| ISOTHANE® 3090A-FRC | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |
| LUVOCOM® 20-8468/SC | LEHVOSS Group | PPA | LUVOCOM® |