Tefzel® HT-2160
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | DuPont Fluoropolymers |
| Trademark: | Tefzel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7EvsKA_Tefzel-HT-2160.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DuPont™ Tefzel ® fluoropolymer HT-2160 resin combines the chemical and high-temperature resistance of Tefzel ® with antistatic levels of electrical conductivity. Tefzel ® HT-2160 and the other Tefzel ® fluoropolymers are melt processible, modified copolymers of ethylene and tetrafluoroethylene. They are high-performance resins that can be processed at relatively high rates compared to other fluoropolymer resins. They are mechanically tough and offer an excellent balance of properties. Tefzel ® HT-2160 can perform successfully in applications where other thermoplastics are lacking in mechanical toughness, broad thermal capability, ability to meet difficult environmental conditions, or limited by fabricating problems. Properly processed products made from virgin Tefzel ® HT-2160 are inert to most solvents and chemicals, hydrolytically stable, and weather resistant. The recommended upper service temperature is 150°C (302°F); useful properties are retained at cryogenic ranges. Mechanical properties include outstanding impact strength and cut-through and abrasion resistance. Typical End Products Tefzel ® HT-2160 resin can be used to manufacture extruded tubing, pipe, and other profiles for hose; linings of components used in the chemical processing industries; industrial film; injection and blow-molded articles requiring superior electrical, chemical, and thermal properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (297°C/5.0 kg) | 2.3 | g/10 min | ASTM D3159 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 34.5 | MPa | ASTM D3159 |
| Tensile Elongation (Break, 23°C) | 200 | % | ASTM D3159 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 255 - 280 | °C | ASTM D3159 |
| Maximum Service Temperature | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1 | 7.0 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Weather and Chemical Resistance: Excellent |
| Note Message | |
|---|---|
| 1 . | Volume resistivity as measured on compression molded plaques. Resistivity is very sensitive to processing technique. Injection molded plaques are typically higher. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers B3 PRTA010 75A UP318 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Generic PI, TP - Carbon Fiber | Generic | PI, TP | Generic |
| LG PVC LK170 | LG Chem Ltd. | PVC Copolymer | LG PVC |
| POLIMAXX 2100N | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| Vipel® F774-NNA-30 | AOC, L.L.C. | Polyester Alloy | Vipel® |