Stat-Rite® E1140
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7EvLZ1_Stat-Rite-E1140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Rite® E1140 is a static dissipative thermoplastic polyurethane (TPU) alloy. Stat-Rite E1140 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite alloys retain uniform static dissipation properties even when injection molded or extruded. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 5.10 | MPa | |
| 300% Strain | 8.00 | MPa | |
| Tensile Strength (Break) | 30.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 670 | % | ASTM D412 |
| Tear Strength | 65.0 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+11 | ohms | ASTM D257 |
| -- 1 | 1.0E+10 | ohms | ESD S11.11 |
| Volume Resistivity | 2.0E+10 | ohms·cm | ASTM D257 |
| Static Decay 2 | |||
| +5000 V to 50 V | 0.9 | sec | |
| -5000 V to -50 V | 0.9 | sec |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | 0.900 | mg/m² | |
| Anions NO3- | 0.0600 | mg/m² | |
| Anions PO4- | 5.00 | mg/m² | |
| Anions SO4- | 0.200 | mg/m² | |
| Outgassing - Total Organics | < 0.100 | ppm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 2.0 to 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | 12% RH |
| 2 . | FTMS-101C, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESN Noir P40 TL | Arkema | Nylon 12 | Rilsamid® |
| Shin-Etsu Elastomer KE-5530U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Hypro® PPC-GF15 NATURAL | Entec Polymers | PP Impact Copolymer | Hypro® |
| Karina IVORY PVC COMPOUND 753-35/ 1-Y-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PP KM-085IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |