| WELNEX™ RMG02 is a Polypropylene Random Copolymer (PP Random Copolymer) product. It is available in Asia Pacific. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 390 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 14.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | > 500 | % | ISO 527-2 |
| Flexural Modulus | 350 | MPa | ISO 178 |
| Flexural Stress | 14.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| 0°C | 10 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 115 | °C | ISO 306 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 90 | ASTM D523 | |
| Haze (1000 µm) | 28 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina COMP. PVC IVORY -E 75930-35/ 1-F-AC-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS CG 310 BLACK 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Petrothene® NA214000 | LyondellBasell Industries | LDPE | Petrothene® |
| Akulon® S225-KS | DSM Engineering Plastics | Nylon 66 | Akulon® |
| For-Tec E OC6OAZ (Series: AD/PAX/CR) | KRAIBURG TPE | TPE | For-Tec E |