ASTALAC™ ASA 306
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7CtiBc_ASTALAC-ASA-306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ASA 306 is a high impact strength grade of ASA suitable for both extrusion and injection moulding applications requiring a combination of impact toughness, abuse resistance, product rigidity and processability. ASA grades show superior colour and property retention compared to ABS. Typical thermoformed applications include advertising signage blanks and caravan panels. Typical injection moulding applications include protective housings for exterior use. Note: The letters "UV" or "W" indicate additional UV stabilisation [ ie: ASTALAC™ ASA 306UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2050 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 62.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 430 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 30.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 77.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 87.0 | °C | |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 to 190 | °C | |
| Cylinder Zone 2 Temp. | 175 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 205 | °C | |
| Cylinder Zone 4 Temp. | 185 to 210 | °C | |
| Cylinder Zone 5 Temp. | 190 to 220 | °C | |
| Die Temperature | 180 to 220 | °C | |
| Take-Off Roll | 75.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC HP5005A | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| TOTAL Polystyrene FT 875 (AS) | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Cereplast Compostables® 2001 | Cereplast, Inc. | PLA | Cereplast Compostables® |
| ExxonMobil™ HDPE HMA 016 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| LUBEMID A26 NATURAL UV | LUBEN PLAST srl | Nylon 66 | LUBEMID |