Adiprene® LF 1900A
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7BrhZA_Adiprene-LF-1900A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE LF 1900A is a TDI-terminated polyester prepolymer having very low free TDI content. This prepolymer also has low viscosity, which allows it to be processed at reduced temperature for better heat stability and longer pot life. It yields a high performance, 90 Shore A hardness elastomer when cured with 4,4'-methylene-bis-(o-chloroaniline), commonly called MBCA. Features of ADIPRENE LF 1900A include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 to 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 1.65 | MPa | |
| 10% Strain | 2.62 | MPa | |
| 15% Strain | 3.62 | MPa | |
| 20% Strain | 4.96 | MPa | |
| 25% Strain | 6.69 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 47.3 | N/mm | ASTM D1938 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 8.27 | MPa | |
| 200% Strain | 10.3 | MPa | |
| 300% Strain | 15.2 | MPa | |
| Tensile Strength | 49.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 105 | kN/m | ASTM D624 |
| Split | 24 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 32 | % | ASTM D395B |
| Bayshore Resilience | 27 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 to 8.0 | min | |
| Demold Time | 30 to 45 | min |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 16 | hr |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7603 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SAMAT 5003N2 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| BCC Resins BC 7136-2 | BCC Products Inc. | Epoxy | BCC Resins |
| ALAMID® 6 V0 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | ALAMID® |
| IDI SMC S20 (Glass Content 10%) | IDI Composites International | TS, Unspecified | IDI SMC |