CALIBRE™ 5101-8
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7A48Yp_CALIBRE-5101-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics:
Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.25 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 62 | ||
| R-Scale | 122 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3380 | MPa | ASTM D638 |
| -- | 3380 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 62.1 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Break 3 | 60.7 | MPa | ASTM D638 |
| Break | 61.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 6.0 | % | ASTM D638 |
| Break | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 3170 | MPa | ASTM D790 |
| -- 6 | 3170 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 93.8 | MPa | ASTM D790 |
| -- 8 | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Instrumented Dart Impact 9(23°C, Total Energy) | 40.1 | J | ASTM D3763 |
| Tensile Impact Strength | 147 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 144 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 134 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/B50, ASTM D1525 10 |
| CLTE - Flow (-40 to 82°C) | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 11 | UL 94 | ||
| 1.59 mm | V-2 | ||
| 3.20 mm | V-0 | ||
| Oxygen Index 12 | 32 | % | ISO 4589-2 |
| Average Extent of Burning | 1 | cm | ASTM D635 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Method I (3 point load), 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 3.39 m/sec |
| 10 . | Rate A (50°C/h), Loading 2 (50 N) |
| 11 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBIT® 1500GN20 | Samyang Corporation | PBT | TRIBIT® |
| DESLON™ 66 DSC201GW3 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| E-RIALGLASS C 07 S 30 G | RIALTI Srl | PP Copolymer | E-RIALGLASS |
| Karina BLACK PVC COMPOUND -E 700-48/1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| CERTENE™ PRM-35C | Muehlstein | PP Random Copolymer | CERTENE™ |