Zytel® HTN FR52G30NHF BK337
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 79qt6K_Zytel-HTN-FR52G30NHF-BK337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide with Improved Flow |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10700 | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | 1.9 | % | ISO 527-2 |
| Flexural Modulus | 9800 | 10800 | MPa | ISO 178 |
| Flexural Stress | 225 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 7.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 35 | kJ/m² | |
| 23°C | 45 | 40 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 281 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 1.8E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.2E-5 | -- | cm/cm/°C | |
| Transverse | 6.2E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 9.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.400 mm | 140 | -- | °C | |
| 0.750 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.400 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.400 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.400 mm | 700 | -- | °C | |
| 3.00 mm | 775 | -- | °C | |
| Oxygen Index | 37 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 LF TFE 15 | RTP Company | PEI | RTP |
| SAMAT 5003D1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Clyrell EC5080 | PolyMirae | TPO (POE) | Clyrell |
| Genestar™ G1500A-M61 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| TOTAL Polypropylene PPR 6290 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |