SLOVAMID® 6 GF 25 LTS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 795AyC_SLOVAMID-6-GF-25-LTS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| With 25% glass fiber reinforced PA 6 for chemical injection molding has increased impact strength and toughness. Use in the production of structural parts for the automotive, electronics, machinery and consumer goods industries such as Holders of electrical hand tools, hobby equipment, gears, housings of electric appliances, mirrors carrier, air screws of the fans, etc. At a higher glass fiber content increases the impact strength, flexural and tensile strength, shrinkage decreases, the thermal application rises to 250°C. GF 60 obtains the module 18000MPa - aluminum alloy values. The product is supplied in natural form or in the colors of the RAL scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.4 | % | |
| Flow | 0.50 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 6100 | MPa | ISO 178 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 26 | kJ/m² | |
| 23°C | 48 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 200 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FHR Polypropylene P6C6B-134 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Gallonprene® GP100-8001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| EMPILON® 610 | EMPILON | SEBS | EMPILON® |
| Karina IVORY PVC COMPOUND 105900-35/ 1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pebax® Rnew 55R53 SP 01 | Arkema | PEBA-Ether | Pebax® Rnew |